Z5CNU17
2020-07-29 09:53:12 Origin： Remark：0 Click：
NF A35-573 Material Specifications of Martensitic Steel Z5CNU17 Round bar, Flat bar, Plate Z5CNU17 ESR remelting technique, Hot forging & rolling, Heat treatment.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - Z5CNU17
MATERIAL CATEGORY - Precipitation hardening stainless steel and heat resisting steel plate
MATERIAL SPECIFICATIONS - NF A35-573
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 15.0 ~ 17.5
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): -
Copper, Cu (％): 3.00 ~ 5.00
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 15.0 ~ 17.5
Nickel, Ni (％): 3.00 ~ 5.00
Molybdenum, Mo (％): -
Copper, Cu (％): 3.00 ~ 5.00
Others (%): Nb+Ta 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER SOLUTION TREATMENT
Steel plate thickness /mm: 0.38～102
Tensile strength, σb≥/MPa: 1255
Yield strength, σ0.2≥/MPa: 1105
Elongation, δ≥(％): 3.0
Hardness |HRC: 38
Hardness |HBS: 363
Yield strength, σ0.2≥/MPa: 1105
Elongation, δ≥(％): 3.0
Hardness |HRC: 38
Hardness |HBS: 363
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Automobile parts, exhaust pipe, Electronics, Turbine motor blade, Bolt and nuts.
Valve sets, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 ~ 1200mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T0.5 ~ 6mm X W100 ~ 1000mm X L1000 ~ 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：Z5CNU17
Previous page：ASTM A182 Gr.F310H
Last page：1.8152
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1