Martensitic Stainless Steel X15CrNi17-03 Round bar, flat bar, and forgings X15CrNi17-03 ESR ingot, Stock Available, Hot forging, Hot rolling, Heat treatment

TECHNICAL DATA SHEET - X15CrNi17-03

TECHNICAL SPECIFICATION: DIN EN 10088-1, 10302

OFFICIAL TEST CERTIFICATE: issued by TUV - SGS

MATERIAL TYPE: Stainless steel
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.12 ~ 0.20
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025

Chromium, Cr (%): 15.0 ~ 18.0

Molybdenum, Mo (%): -

Nickel, Ni (%): 2.00 ~ 3.00

MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 880 ~ 1080
Yield strength, Rp0.2 ≥ MPa: 690
Elongation, A5 ≥ (％): 12.0
Reduction of area, Z ≥ (％): -
Impact, AKv (J/cm2): -
Annealed hardness | HB: 262 ~ 326

Quenching, 1010,+/-10 Deg, tempering 605, +/-5 Deg.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm

Forged plate: T90 ~ 400 X W50 ~ 1200 X Length
Steel strip: T0.20 ~ 3mm X W10 ~ 1200mm X Coil
Forging piece: stepped shafts, other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.

Hot search：X15CrNi17-03

Previous page：F316H
Last page：AMS 5502

Share to：

X15CrNi17-03
2024-11-05 10:52:00 Origin： Remark：0 Click：

Total list

Monthly rank

X15CrNi17-03 2024-11-05 10:52:00 Origin： Remark：0 Click：

Total list

Monthly rank

X15CrNi17-03
2024-11-05 10:52:00 Origin： Remark：0 Click：