TECHNICAL DATA SHEET - ASTM A182 Grade F316L
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 17Cr - 13Ni Austenitic Stainless steel
CHEMICAL COMPOSITION (mass weight - %)
C (％):  ≤ 0.030
Mn (％):  ≤ 2.00
Si (％):  ≤ 1.00
P (％)≤:  0.035
S (％)≤:  0.020
Cr (%):  16.0 ~ 18.0
Mo (%):  2.00 ~ 3.00
Ni (%):  10.0 ~ 14.0
Nb (%):  -
Ti (%):  -
N (%):  ≤ 0.10
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 485
Yield strength, σ0.2/MPa: 175
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing
Cooling medium: water or oil cooling 
Tempering temperature: 1040 Deg.C
PRODUCT DESCRIPTION
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.