X3CrNi13-4
2020-09-03 16:29:39 Origin: Remark:0 Click:
Description X3CrNi13-4 datasheet, X3CrNi13-4 Chemical, X3CrNi13-4 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATA SHEET - DIN X3CrNi13-4
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.05
Si (%)≤: 0.70
Mn (%)≤: 1.50
P (%)≤: 0.040
S (%)≤: 0.015
Cr (%): 12.0~14.0
Ni (%): 3.50~4.50
Mo (%): 0.30~0.70
Other(%): N ≥ 0.020
Si (%)≤: 0.70
Mn (%)≤: 1.50
P (%)≤: 0.040
S (%)≤: 0.015
Cr (%): 12.0~14.0
Ni (%): 3.50~4.50
Mo (%): 0.30~0.70
Other(%): N ≥ 0.020
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: heat treatment
Thickness/mm: 160~25
Thickness/mm: 160~25
Tensile strength, σb/MPa: 650~830
Yield strengt, σ0.2≥/MPa: 520
Elongation, δ5≥(%): 15/12
Reduction of area, ψ≥(%): —
Impact strength, Akv≥/J: 70/50
Yield strengt, σ0.2≥/MPa: 520
Elongation, δ5≥(%): 15/12
Reduction of area, ψ≥(%): —
Impact strength, Akv≥/J: 70/50
/40Hardness HBS30: -
Condition: heat treatment
Thickness/mm: 160~25
Thickness/mm: 160~25
σb/MPa: 780~980
σ0.2≥/MPa: 620
δ5≥(%): 15/12
ψ≥(%): —
Akv≥/J: 70/50
σ0.2≥/MPa: 620
δ5≥(%): 15/12
ψ≥(%): —
Akv≥/J: 70/50
Hardness HBS30: -
Thickness/mm: 160~25
σb/MPa: 900~1100
σ0.2≥/MPa: 800
δ5≥(%): 12/10
ψ≥(%): —
Akv≥/J: 50/40
σ0.2≥/MPa: 800
δ5≥(%): 12/10
ψ≥(%): —
Akv≥/J: 50/40
Hardness HBS30: -
AVAILABILITY
Round bar / flat bar / steel strip / square bar / forge piece
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / steel strip / square bar / forge piece
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200 mm, with wall thickness ranging from 15 to 350 mm.
Pipes / Tubings: OD30 - 1200 mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Hot search:X3CrNi13-4
Previous page:ASTM A890 Gr.3A
Last page:ASTM A890 Gr.4A
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1