F347H
2020-12-28 09:00:55   Origin:   Remark:0 Click:

Specifications F347H Round bar, Forgings F347H Flat Bar Plate Heat treatment Machined, Technical standards - ASTM A182 - 2018.or by agreement.
TECHNICAL DATA SHEET - ASTM A182 Grade F347H

MATERIAL TECHNICAL STANDARDS - ASTM A182 - 2018
MATERIAL TYPE - 18Cr 10Ni Austenitic Stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%):  0.04 ~ 0.10
Manganese, Mn (%):  ≤ 2.00
Silicon, Si (%):   ≤ 1.00
Phosphorus, P (%)≤:  0.030
Sulfur, S (%)≤:  0.010
Nickel, Ni (%):  9.00 ~ 13.0
Chromium, Cr (%):  17.0 ~ 20.0
Molybdenum, Mo (%):  -
Niobium, Nb (%):  10 X C ~ 1.10
Nitrogen, N (%):  -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa:  515
Yield strength, σ0.2/MPa:  205
Elongation, δ ≥(%): 30.0
Reduction of area, ф ≥ (%): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing
Cooling medium: water or oil cooling
Tempering temperature: 1010 ~ 1050 Deg.C
PRODUCT MELTING & AVAILABLE DIMENSIONS
The
alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 450mm
Square bar / Flat bar: 10mm to 1000mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry, pleased to E-mail (
sales@ccsteels.com) our resident team of qualified production engineers.

Hot search:F347H

Previous page:A514 Grade S
Last page:1.2059

Share to: