Martensitic Steel 10705AJ Round bar, Flat bar, Forgings 10705AJ Stock Available Hot forging / rolling, Heat treatment, Cold working
SPECIFICATIONS DATASHEET - Grade 10705AJ
Official test certification - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.12 ~ 0.16
Silicon, Si (%): ≤ 0.10
Manganese, Mn (%): 0.36 ~ 0.70
Phosphorus, P (%)≤: 0.020
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 10.00 ~ 11.0
Nickel, Ni (%): 0.35 ~ 0.65
Molybdenum, Mo (%): 0.30 ~ 0.50
Silicon, Si (%): ≤ 0.10
Manganese, Mn (%): 0.36 ~ 0.70
Phosphorus, P (%)≤: 0.020
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 10.00 ~ 11.0
Nickel, Ni (%): 0.35 ~ 0.65
Molybdenum, Mo (%): 0.30 ~ 0.50
Tungsten, W (%): 1.50 ~ 1.90
Vanadium, V (%): 0.14 ~ 0.20
Niobium, Nb (%): 0.05 ~ 0.11
Nitrogen, N (%): 0.04 ~ 0.08
Copper, Cu (%): ≤ 0.10
MECHANICAL PROPERTIES UNDER DIFFERENT HEAT TREATED CONDITIONS
Form: Bar, Flat bar, Forge piece
Condition: Q + T 675℃
Tensile strentgh, Rm / MPa: 930
Yield strength, Rp0.2 / MPa: 760
Yield strength, Rp0.2 / MPa: 760
Elongation, A5 (%): 14.0
Reduction of area, Z (%): 32.0
Hardness | HRB: 277 ~ 331
Reduction of area, Z (%): 32.0
Hardness | HRB: 277 ~ 331
Impact Value (V-Notch charpy), RT: 20J
HEAT TREATMENT PRACTICE
Quenching: 1100 ℃ min., oil cooled
Tempering: 650 ℃ min., air cooled
Stress relieving: 620 ℃
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
FORMS & AVAILABLE DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 500mm
Square bar / Flat bar: 6mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (diameter): 5.5mm to 500mm
Square bar / Flat bar: 6mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T30 ~ 400mm X W50 ~ 1500mm X L1000 ~ 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search:10705AJ
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1