KS D3731 Specifications STR 616 Flat bar, Bolts and nuts STR 616 Forgings Heat treatment, Straightening, Ultrasonic flaw detection test, Cold worked.
TECHNICAL DATA SHEET - KS D3731 Grade STR 616
TECHNICAL SPECIFICATIONS - KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel bar and plate
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel bar and plate
HS code for Customs: 72221100 / 7219 1100
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 13.0
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (%): 0.75 ~ 1.25
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 13.0
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (%): 0.75 ~ 1.25
Tungsten, W (%): 0.75 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
Nitrogen, N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1020 ~ 1070 Deg.C, air or oil cooled
Nitrogen, N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1020 ~ 1070 Deg.C, air or oil cooled
Aged 600 Deg. C Min., air cooling
Tensile strength, σb/ ≥ MPa: 885
Yield strength, σ0.2/ ≥ MPa: 735
Elongation, δ (％) ≥: 10.0
Reduction of area, ф (％) ≥: 25.0
Hardness ≤ (HBW): 341 Max.
Tensile strength, σb/ ≥ MPa: 885
Yield strength, σ0.2/ ≥ MPa: 735
Elongation, δ (％) ≥: 10.0
Reduction of area, ф (％) ≥: 25.0
Hardness ≤ (HBW): 341 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS AND DIMENSIONS AVAILABLE
Round bar & Disc (diameter): 5.5 ~ 600mm
Wire rod (Diameter): 5.5 ~ 13mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS AND DIMENSIONS AVAILABLE
Round bar & Disc (diameter): 5.5 ~ 600mm
Wire rod (Diameter): 5.5 ~ 13mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：EN52 & EN 52
Last page：STR616
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1