Martensitic steel 1.4528 Round bar, flat bar, EF / VIM, ESR & VAR technique, 1.4528 Hot forging / rolling, Heat treatment, Straighted, 100% Ultrasonic flaw detection test, cold machined.
TECHNICAL DATA SHEET - Grade DIN/EN 1.4528
HS CODE FOR CUSTOMS - 72222000 / 72221100
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Stainless steel bar and forgings
CHEMICAL COMPOSITION (mass weight % )
Carbon, C (％): 1.00 ~ 1.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 16.5 ~ 18.5
Nickel, Ni (％): -
Molybdenum, Mo (%): 1.00 ~ 1.50
Cobalt, Co (%): 1.30 ~ 1.80
MATERIAL CATEGORY - Stainless steel bar and forgings
CHEMICAL COMPOSITION (mass weight % )
Carbon, C (％): 1.00 ~ 1.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 16.5 ~ 18.5
Nickel, Ni (％): -
Molybdenum, Mo (%): 1.00 ~ 1.50
Cobalt, Co (%): 1.30 ~ 1.80
Vanadium, V (%): 0.07 ~ 0.12
MECHANICAL PROPERTY UNDER ROOM TEMP.
Annealing temp.: 800 ~ 850, furnace cooled
MECHANICAL PROPERTY UNDER ROOM TEMP.
Annealing temp.: 800 ~ 850, furnace cooled
Tensile strength, σb/ ≥ MPa: -
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 285 Max.
METHOD OF MELT PROCESS
The alloy is usually produced by EF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS & SIZES AVAILABLE
Round bar (Diameter): 5.5 ~ 350mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 500mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 285 Max.
METHOD OF MELT PROCESS
The alloy is usually produced by EF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS & SIZES AVAILABLE
Round bar (Diameter): 5.5 ~ 350mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 500mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Hot search：1.4528
Previous page：AMS 5743J
Last page：X105CrCoMo18-2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1