Aerospace AMS 5549F Specifications, Datasheet AMS 5549F Chemical, AMS 5549F Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL STANDARD - AMS 5549F
MATERIAL CATEGORY - High Alloy Aerospace Material Steel Series
TECHNICAL SPECIFICATION - AMS 5549F
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.10 ~ 0.15
TECHNICAL SPECIFICATION - AMS 5549F
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.10 ~ 0.15
Mn (％): 0.50 ~ 1.25
Si (％): ≤ 0.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 16.0
Si (％): ≤ 0.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 16.0
Mo (%): 2.50 ~ 3.25
Ni (％): 4.00 ~ 5.00
N (%): 0.07 ~ 0.13
Ni (％): 4.00 ~ 5.00
N (%): 0.07 ~ 0.13
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: plate, sheet, strip
Tensile strength, σb/MPa: 1140
Yield strength, σ0.2/MPa: 965
Form: plate, sheet, strip
Tensile strength, σb/MPa: 1140
Yield strength, σ0.2/MPa: 965
Elongation, δ(％): 12.0
Reduction of area, ф(％): -
Hardness + Annealed (HB): HRC37 ~ 43 (AT + aged)
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Reduction of area, ф(％): -
Hardness + Annealed (HB): HRC37 ~ 43 (AT + aged)
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1