S63014
2021-03-29 13:48:00 Origin: Remark:0 Click:
Valve steel S63014 Specifications, Datasheet S63014 Chemical, S63014 Properties Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - Grade UNS S63014
HS CODE - 72221100 / 72221900
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.30 ~ 0.45
Si (%): 2.75 ~ 3.25
Mn (%): 0.80 ~ 1.30
P (%)≤: 0.045
S (%)≤: 0.030
Cr (%): 18.0 ~ 20.0
Ni (%): 7.50 ~ 8.50
Mo (%): -
Si (%): 2.75 ~ 3.25
Mn (%): 0.80 ~ 1.30
P (%)≤: 0.045
S (%)≤: 0.030
Cr (%): 18.0 ~ 20.0
Ni (%): 7.50 ~ 8.50
Mo (%): -
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Hot forming temperature /℃: 1100~980
Heat treatment temperature and cooling method | annealed: -
Heat treatment temperature and cooling method | quenched: 1150~1180 Water
Heat treatment temperature and cooling method | tempered: 800~830
Mechanical property, tensils strength, |σb/MPa: 885
Mechanical property yield strength, |σs≥/MPa: 545
Mechanical property elongation, |δ5≥(%): 25.0
Mechanical property reduction of area, |ψ≥(%): 40.0
Hot forming temperature /℃: 1100~980
Heat treatment temperature and cooling method | annealed: -
Heat treatment temperature and cooling method | quenched: 1150~1180 Water
Heat treatment temperature and cooling method | tempered: 800~830
Mechanical property, tensils strength, |σb/MPa: 885
Mechanical property yield strength, |σs≥/MPa: 545
Mechanical property elongation, |δ5≥(%): 25.0
Mechanical property reduction of area, |ψ≥(%): 40.0
METHOD OF MELTING PROCESS
Valve steel is generally smelt in electric arc furnace EAF or AOD. For higher quality, it should be smelt via technology of vacuum refining and external refining.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 450mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 450mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Forgings: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Forgings: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search:S63014
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1