X3MnCrNiMoN20-13
2021-04-03 10:11:28 Origin： Remark：0 Click：
Description X3MnCrNiMoN20-13 Flat bar, On stock X3MnCrNiMoN20-13 Forgings, X3MnCrNiMoN20-13 Ring Melting, ESR & VAR technique, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - X3MnCrNiMoN20-13
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - non-magnetic stainless steel bar and forgings
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7222 1100 / 7220 1100 / 7220 2030
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): 0.30 ~ 0.60
Manganese, Mn (％): 18.5 ~ 22.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 13.0 ~ 16.0
Nickel, Ni (％): 0.25 ~ 0.50
Molybdenum, Mo (%): 0.35 ~ 0.60
Nitrogen, N (%): 0.32 ~ 0.40
MATERIAL CATEGORY - non-magnetic stainless steel bar and forgings
MELTING PROCESS - Consumable electrode remelted
H S CODE For Customs - 7222 1100 / 7220 1100 / 7220 2030
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): 0.30 ~ 0.60
Manganese, Mn (％): 18.5 ~ 22.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 13.0 ~ 16.0
Nickel, Ni (％): 0.25 ~ 0.50
Molybdenum, Mo (%): 0.35 ~ 0.60
Nitrogen, N (%): 0.32 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: anneal treated 1050 ~ 1150 Deg.C
Tensile strength, Rm ≥ MPa: 900
Yield strength, Rp0.2 ≥ MPa: 770
Elongation, A5 (％) ≥: 25.0
Reduction of area, Z (％) ≥: -
Hardness ≤ (HBW): 277 Min.
METHOD OF MELT
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar / rod / disc (diameter): 5.5 ~ 800mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Condition: anneal treated 1050 ~ 1150 Deg.C
Tensile strength, Rm ≥ MPa: 900
Yield strength, Rp0.2 ≥ MPa: 770
Elongation, A5 (％) ≥: 25.0
Reduction of area, Z (％) ≥: -
Hardness ≤ (HBW): 277 Min.
METHOD OF MELT
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar / rod / disc (diameter): 5.5 ~ 800mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：X3MnCrNiMoN20-13
Previous page：AMS 5552
Last page：Magnadur 501
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1