N02201
2021-04-08 10:17:39 Origin： Remark：0 Click：
Specifications N02201 Datasheet, N02201 Chemical, N02201 Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL STANDARD - Grade N02201
MATERIAL CATEGORY - High Alloy Aerospace Material Steel Series
TECHNICAL SPECIFICATION - AMS 5553G
HSN CODE - 75051100
TECHNICAL SPECIFICATION - AMS 5553G
HSN CODE - 75051100
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): ≤ 0.02
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): ≤ 0.02
Mn (％): ≤ 0.35
Si (％): ≤ 0.35
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): -
Si (％): ≤ 0.35
P (％)≤: 0.020
S (％)≤: 0.010
Cr (％): -
Ni (%): 99.0 Min.
Mo (％): -
Mo (％): -
Co (%): ≤ 1.00
Al (％): -
Cu (%): ≤ 0.25
Cu (%): ≤ 0.25
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: bars and forgings
Tensile strength, σb/MPa: 345
Yield strength, σ0.2/MPa: 207
Form: bars and forgings
Tensile strength, σb/MPa: 345
Yield strength, σ0.2/MPa: 207
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness + solution annealed (HB): 66HRB Max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Reduction of area, ф(％): -
Hardness + solution annealed (HB): 66HRB Max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：N02201
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1