ASTM A565 type 616
2021-06-02 18:54:53 Origin： Remark：0 Click：
Inventory AISI 616 Flat bar, Turbine blade A565 Grade 616, Specifications S42200 hot forging Heat treated, Properties from Steelmelting (ESR refined).
RAW MATERIAL DESIGNATION - ASTM A565 type 616
Ex-stock & Dimensions - Diameter 20 ~ 240mm, ESR ingot, plate
Material technical standards - ASTM A565
Official Test Certificate - issued by TUV - SGS - BV
Material technical standards - ASTM A565
Official Test Certificate - issued by TUV - SGS - BV
Method of melting - BEF + AOD + ESR / VAR
HS Code for Customs - 72221100 / 72222000 / 72221900
Typical Chemical Elements - mass weight (%)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Vanadium, V (％): 0.20 ~ 0.30
Tungsten, W (%): 0.90 ~ 1.25
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: bar, flat bar, forgings
Condition + H: Tempering (620℃)
Tensile strength, σb / MPa: 965 min.
Yield strength, σ0.2 / MPa: 760 min.
Elongation, δ5 (％): 13.0 min
Reduction of area, ф (％): 30.0
Hardness | HRB: 302 ~ 352
Condition + HT: Tempering (675℃)
Tensile strength, σb / MPa: 825 min.
Yield strength, σ0.2 / MPa: 585 min.
Elongation, δ5 (％): 17.0 min.
Reduction of area, ф (％): 35.0 min.
Hardness | HRB: 241 ~ 285
Typical Chemical Elements - mass weight (%)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Vanadium, V (％): 0.20 ~ 0.30
Tungsten, W (%): 0.90 ~ 1.25
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: bar, flat bar, forgings
Condition + H: Tempering (620℃)
Tensile strength, σb / MPa: 965 min.
Yield strength, σ0.2 / MPa: 760 min.
Elongation, δ5 (％): 13.0 min
Reduction of area, ф (％): 30.0
Hardness | HRB: 302 ~ 352
Condition + HT: Tempering (675℃)
Tensile strength, σb / MPa: 825 min.
Yield strength, σ0.2 / MPa: 585 min.
Elongation, δ5 (％): 17.0 min.
Reduction of area, ф (％): 35.0 min.
Hardness | HRB: 241 ~ 285
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 550mm
Steel strip / Sheet: THK0.5 ~ 3.0mm, Width 10 ~ 200mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 550mm
Steel strip / Sheet: THK0.5 ~ 3.0mm, Width 10 ~ 200mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1