Material standards EN 56CM Datasheet, Ex-stock 56CM Chemical, 56CM Properties Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade EN56CM
MELTING PROCESS - Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.18 ~ 0.25
Mn (％): 1.20 ~ 1.80
Si (％): ≤ 1.50
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 12.0 ~ 14.0
Ni (%): ≤ 1.50
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 540
C (％): 0.18 ~ 0.25
Mn (％): 1.20 ~ 1.80
Si (％): ≤ 1.50
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 12.0 ~ 14.0
Ni (%): ≤ 1.50
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 540
Yield strength, σ0.2/≥ MPa: 345
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥(％): 55.0
Hardness in condition of annealing +A: HB165
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Reduction of area, ф ≥(％): 55.0
Hardness in condition of annealing +A: HB165
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：56CM
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1