X5CrNiCuNb17-4-4
2021-08-13 10:55:36 Origin： Remark：0 Click：
Description X5CrNiCuNb17-4-4 Flat bars, Stocklist X5CrNiCuNb17-4-4 Shaft, X5CrNiCuNb17-4-4 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
RAW MATERIAL SPECIFICATIONS - Grade EN X5CrNiCuNb17-4-4
SPECIAL MELTING PROCESS - EAF + AOD + ESR
MATERIAL CATEGORY - Stainless steel round bar, wire rod, and semi-finished products
HS Code For Customs - 72221100 / 72221900 / 72222000
MATERIAL SPECIFICATIONS - BS EN 10088-3
CHEMICAL COMPOSITION (Mass Weight - %)
C (％): ≤ 0.055
Si (％): ≤ 1.00
Mn (％): ≤ 0.50
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 15.0 ~ 16.0
Ni (％): 3.00 ~ 4.50
Mo (％): ≤ 0.60
Nb (％): 0.15 ~ 0.35
Si (％): ≤ 1.00
Mn (％): ≤ 0.50
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 15.0 ~ 16.0
Ni (％): 3.00 ~ 4.50
Mo (％): ≤ 0.60
Nb (％): 0.15 ~ 0.35
Cu (%): 3.00 ~ 3.70
MECHANICAL PROPERTIES AND HEAT TREATMENT CYCLE
Thickness/≤mm: 100
Condition of thermal treatment: AT (Solution treatment)
Hardness ≤HBS: 360
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: ≤1200
Elongation δ ≥(％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J : -
Hardness ≤HBS: 360
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: ≤1200
Elongation δ ≥(％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J : -
Condition of thermal treatment: P930
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 720
Tensile strength σb/MPa: 930~1100
Elongation δ ≥(％): -16
Impact absorbing power Akv≥/J : 40
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 720
Tensile strength σb/MPa: 930~1100
Elongation δ ≥(％): -16
Impact absorbing power Akv≥/J : 40
Condition of thermal treatment: P960
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 790
Tensile strength σb/MPa: 960~1160
Elongation δ ≥(％): 12
Impact absorbing power Akv≥/J : -
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 790
Tensile strength σb/MPa: 960~1160
Elongation δ ≥(％): 12
Impact absorbing power Akv≥/J : -
Those materials are widely used in manufacturing the high strength, anti-corrosive forge piece for planes, gas turbine and other machined parts.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
The alloy is usually produced by EAF AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T60 - 400mm X W70 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：X5CrNiCuNb17-4-4
Previous page：STS301J1
Last page：Z5CNU17-4PH
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1