Specifications EN 58J Datasheet, Stocklist EN 58J Chemical, Inventory EN 58J Suppliers Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade EN 58J
MATERIAL CATEGORY - Stainless steel 18%Cr / 10%Ni / 3%Mo
TECHNICAL SPECIFICATION - BS970 Part 6
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS ( Mass Weight - %)
C (％): 0.07 ~ 0.16
Mn (％): 1.70 ~ 2.50
Si (％): 0.15 ~ 0.50
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 17.0 ~ 20.0
Ni (%): 9.00 ~ 12.0
C (％): 0.07 ~ 0.16
Mn (％): 1.70 ~ 2.50
Si (％): 0.15 ~ 0.50
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 17.0 ~ 20.0
Ni (%): 9.00 ~ 12.0
Mo (%): 2.50 ~ 3.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 520
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 520
Yield strength, σ0.2/≥ MPa: 245
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB269
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 550mm
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB269
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 550mm
Rolled / forged plate: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1