EN 61
2021-10-11 10:53:21 Origin： Remark：0 Click：
Specifications EN 61 Round bar, flat bar Stocklist EN 61 Hot forging, Hot rolling, Heat treated, 100% Ultrasonic flaw detection test, Cold working or machined.
TECHNICAL DATA SHEET - Grade EN 61
MATERIAL CATEGORY - Stainless steel 21%Cr / 0.25%Ni
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.12
Manganese, Mn (％): ≤ 1.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (%): 20.0 ~ 22.0
Nickel, Ni (%): ≤ 0.50
Molybdenum, Mo (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:
Tempering temperature /℃:
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 205
Elongation, δ ≥(％): 22.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB235
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 500mm
Rolled / forged plate: 10mm to 1000mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
MATERIAL CATEGORY - Stainless steel 21%Cr / 0.25%Ni
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.12
Manganese, Mn (％): ≤ 1.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (%): 20.0 ~ 22.0
Nickel, Ni (%): ≤ 0.50
Molybdenum, Mo (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:
Tempering temperature /℃:
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 205
Elongation, δ ≥(％): 22.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB235
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 500mm
Rolled / forged plate: 10mm to 1000mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1