TECHNICAL DATA SHEET - UNS S41000
MATERIAL CATEGORY - Martensite type steel - 13Cr
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 11.5 ~ 13.5
Ni (％): ≤ 0.75
Mo (％): -
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: plate,sheet,strip
Condition: annealing
Tensile strength, σb/MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, δ(％): 20
Reduction of area, ф(％): 45
Hardness | HRB:
PRODUCT DESCRIPTION & MELTING
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Black bar / flat bar / steel strip / square bar / valve body / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1200mm
Plate / Sheet steel / Steel strip: 0.1mm to 1500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
MATERIAL CATEGORY - Martensite type steel - 13Cr
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 11.5 ~ 13.5
Ni (％): ≤ 0.75
Mo (％): -
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: plate,sheet,strip
Condition: annealing
Tensile strength, σb/MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, δ(％): 20
Reduction of area, ф(％): 45
Hardness | HRB:
PRODUCT DESCRIPTION & MELTING
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Black bar / flat bar / steel strip / square bar / valve body / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1200mm
Plate / Sheet steel / Steel strip: 0.1mm to 1500mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search：S41000
Previous page：AISI 410
Last page：UNS S41005
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1