410Cb / XM-30
2014-10-13 11:23:25 Origin： Remark：0 Click：
410Cb (S41040), is a Martensitic 12.0% Chromium base Stainless steel, XM-30 Round bar, flat bar, and forgings From Steel melting, ESR melted, Hot forging/ rolling, Heat treated, 100% Ultrasonic test, Cold machined.
MATERIAL TECHNICAL DATASHEET - ASTM XM-30 / 410Cb / UNS S41040
MATERIAL CATEGORY - Martensite type - 12Cr - Nb
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.15
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 11.5 ~ 13.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Niobium, Nb (％): 0.05 ~ 0.30
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 11.5 ~ 13.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Niobium, Nb (％): 0.05 ~ 0.30
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: round bar, flat bar
Condition: annealing + hot forging
Tensile strength, σb/MPa: 485
Yield strength, σ0.2/MPa: 275
Yield strength, σ0.2/MPa: 275
Elongation, δ (％): 13.0
Reduction of area, ф (％): 45.0
Hardness | HRB: -
Reduction of area, ф (％): 45.0
Hardness | HRB: -
Form: bar
Condition: annealing +cold roll/drawn
σb/MPa: 485
σ0.2/MPa: 275
σ0.2/MPa: 275
δ(％): 12
ф(％): 35
Hardness | HRB: -
ф(％): 35
Hardness | HRB: -
TYPICAL APPLICATIONS
Chemical equipment & parts. Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
PRODUCT PROFILE & DIMENSIONS
Mechanical parts used in the condition of corrosion resistance.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 2000mm
Plate / Sheet steel / Steel strip: 0.5mm to 2000mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 10mm to 2000mm
Plate / Sheet steel / Steel strip: 0.5mm to 2000mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1