S41600
2014-10-14 10:53:05   Origin：   Remark：0 Click：

ATERIAL CATEGORY - Martensite type - 13Cr
CHEMICAL COMPOSITION (WEIGHT %)
C (％):     ≤ 0.15
Si (％):     ≤ 1.00
Mn (％):   ≤ 1.25
P (％)≤:   0.060
S (％)≤:   ≥ 0.15
Cr (％):    12.0 ~ 14.0
Ni (％):     -
Mo (％):   -
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: forging piece
Condition:  annealing
Tensile strength, σb/MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, δ(％):  20
Reduction of area, ф(％): 45
Hardness | HRB:  -
Form: wire
Condition:  annealing
σb/MPa:   585~860
σ0.2/MPa:    -
δ(％):    -
ф(％):   -
Hardness | HRB:  -

PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
AVAILABILITY
Round bar / Flat bar / Steel strip / Square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632, A176, A580
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel

PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com