Z8CNT18-10 is Austenitic stainless steel EN X6CrNiTi18-10 Wire rod - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS EN 10088-3 (2005) or by agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade NF Z8CNT18-10
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE: Austenitic series
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (Mass weight %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): 9.00 ~ 12.0
Mo (％): -
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): 9.00 ~ 12.0
Mo (％): -
Ti (％): 5×C～0.70
MECHANICAL PROPERTIES VIA SOLUTION TREATMENT
Thickness Diameter (d)/≤mm: 160
Hardness HBS: 215
Yield strength σ0.2≥/MPa: 190
Tensile strength σb/MPa: 500～700
Yield strength σ0.2≥/MPa: 190
Tensile strength σb/MPa: 500～700
Elongation δ(longitudinal )≥(％): 40
Elongation δ(transversal )≥(％): -
Impact absorbing energy Akv≥/J|longitudinal: 100
Impact absorbing energy Akv≥/J|transversal: -
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
Impact absorbing energy Akv≥/J|transversal: -
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
Thickness Diameter (d)/≤mm: 160<d≤250
Hardness HBS: 215
Yield strength σ0.2≥/MPa: 190
Tensile strength σb/MPa: 500～700
Elongation δ(longitudinal )≥(％): -
Yield strength σ0.2≥/MPa: 190
Tensile strength σb/MPa: 500～700
Elongation δ(longitudinal )≥(％): -
Elongation δ(transversal )≥(％): 30
Impact absorbing energy Akv≥/J|longitudinal: -
Impact absorbing energy Akv≥/J|transversal: 60
Intergranular corrosion resistance tendency | condition of delivery: YesImpact absorbing energy Akv≥/J|transversal: 60
Intergranular corrosion resistance tendency | condition of welding: Yes
AUSTENITIC STAINLESS STEEL APPLICATION
The chromium content is 18%, or so 8% nickel and elements of Molybdenum, Titanium, Nitrogen. Combination property is pretty well, can be corrosive for multiple mediums. Those steels possess excellent plasticity, toughness,weldability,corrosion resistance and Non-magnetism or weak magnetism, and good corrosion resistance in the medium of oxidability and reducibility, which are for processing the acid-resistant equipments, such as anti-corrosive vessel, equipment lining, running piping, equipment parts of nitric acid resistance, and also for main material of stainless steel horologe accessories. Austenitic stainless steel adopts solution treatment generally, that's to say, heating the steel to 1050～1150℃, then water cooling or wind cooling, to obtain single phase austenite structure.
PRODUCT DESCRIPTIONThe alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5 to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5 to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X Lmm
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000 X Lmm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：Z8CNT18-10
Previous page：AMS 5627
Last page：SAE 51430 Ferritic Stainless Steel
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1