AMS 5669 Alloy Round bar, Flat bar, Plate, AMS 5669 corrosion and heat resistant nickel base 15.5 Cr - 0.95 (Cb + Ta) - 2.5Ti - 0.7Al - 7.0Fe consumable electrode or vacuum induction melted.
MATERIAL TECHNICAL DATASHEET - Grade AMS 5669
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5669
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 0.35
Silicon, Si (％): ≤ 0.35
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): 70.0 Min.
Molybdenum, Mo (%): -
Niobium, Nb (%): 0.70 ~ 1.20
Titanium, Ti (%): 2.25 ~ 2.75
Aluminum, Al (%): 0.40 ~ 1.00
Coppper, Cu (%): ≤ 0.50
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): 5.00 ~ 9.00
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5669
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 0.35
Silicon, Si (％): ≤ 0.35
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): 70.0 Min.
Molybdenum, Mo (%): -
Niobium, Nb (%): 0.70 ~ 1.20
Titanium, Ti (%): 2.25 ~ 2.75
Aluminum, Al (%): 0.40 ~ 1.00
Coppper, Cu (%): ≤ 0.50
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): 5.00 ~ 9.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Shapes: bars, forgings and rings.
Heat treatment practice: solution heat treated by heating to 982 °C ± 14 °C,
holding at heat for 1 hour, and cooling in air.
Aged at 621 °C ± 8.3 °C, holding for 8 hours, and air cooling.
Tensile strength, σb/MPa: 1150
Yield strength, σ0.2/MPa: 793
Elongation, δ(％): 15.0
Reduction of area, ф (％): 20.0
Hardness under hot finished condition | HBW: -
Hardness under precipitation heat treatment condition | HBW: HRC 32 ~ 42.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 550mm
Square bar / Flat bar (Thickness X width): 10 to 550mm
Wire rod (Diameter): 1.0 to 13.0mm
Steel strip: THK0.5 ~ 3.0, width 10 ~ 220mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Tensile strength, σb/MPa: 1150
Yield strength, σ0.2/MPa: 793
Elongation, δ(％): 15.0
Reduction of area, ф (％): 20.0
Hardness under hot finished condition | HBW: -
Hardness under precipitation heat treatment condition | HBW: HRC 32 ~ 42.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 550mm
Square bar / Flat bar (Thickness X width): 10 to 550mm
Wire rod (Diameter): 1.0 to 13.0mm
Steel strip: THK0.5 ~ 3.0, width 10 ~ 220mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Previous page：75NiCrMo5-3-3
Last page：1.2777
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1