ASTM 420FSe Global Wholesaler Blade Steel, ASTM 420FSe Alloy Suppliers & Manufacturers, ASTM 420FSe Forge bar plate machined, ASTM 420FSe Alloy exporter. Technical specifications - ASTM A276 / 2006.
DATA SHEET - ASTM 420FSe & UNS S42023
MATERIAL CATEGORY: Martensite type 13Cr
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632, A176, A580
ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.20 ~ 0.40
Si (％): ≤ 1.00
Mn (％): ≤ 1.25
P (％)≤: 0.060
S (％)≤: 0.060
Cr (％): 12.0 ~ 14.0
Ni (％): —
Mo (％): ≤ 0.50
Other (％): Se ≥ 0.15
Si (％): ≤ 1.00
Mn (％): ≤ 1.25
P (％)≤: 0.060
S (％)≤: 0.060
Cr (％): 12.0 ~ 14.0
Ni (％): —
Mo (％): ≤ 0.50
Other (％): Se ≥ 0.15
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT)
Form: bar,forge piece
Condition: Tempering (620℃)
σb/MPa: 965
σ0.2/MPa: 760
σ0.2/MPa: 760
δ(％): 13
ф(％): 30
Hardness | HRB: -
ф(％): 30
Hardness | HRB: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 5000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 5000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1