Technical specifications of UNS S43100 Martensite steel, round bar, disc, flat bar, and forgings, ESR ingot, steelmaking, hot forging, rolling, heat treatment
TECHNICAL DATA SHEET - AISI 431 & UNS S43100
MATERIAL CATEGORY: Martensite type 16Cr-2Ni
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (%): ≤ 0.20
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 15.0~17.0
Nickel, Ni (%): 1.25~2.50
Molybdenum, Mo (%): -
Ferrum, Fe (%): -
Carbon, C (%): ≤ 0.20
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 15.0~17.0
Nickel, Ni (%): 1.25~2.50
Molybdenum, Mo (%): -
Ferrum, Fe (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: forge piece
Condition: medium tempering
Tensile strength, Rm / MPa: 795
Yield strength, Rpσ0.2 / MPa: 620
Yield strength, Rpσ0.2 / MPa: 620
Elongation, δ5 (%): 15
Reduction of area, ф %): -
Hardness | HRB: -
Reduction of area, ф %): -
Hardness | HRB: -
Form: wire
Condition: annealing
σb / MPa: 760
σ0.2 / MPa: -
σ0.2 / MPa: -
δ5 (%): -
ф (%): -
Hardness | HRB: -
ф (%): -
Hardness | HRB: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
PRODUCT PROFILE
Rod / round bar / disc (diameter): 5.5mm to 880mm
Square bar / flat bar: 8mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Square bar / flat bar: 8mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Total list
Monthly rank
- 53Z15CN17-03
- 39ASTM A565 type 616HT
- 32X35CrMo17
- 2710705MBU
- 26FV535
- 23X8CrMnN18-18
- 23P550
- 21Z8CND17-04
- 21N06102
- 21X2Cr11 / 1.4003