DIN SEW 390 (1991) Material Specifications Austenitic Steel X35Mn18 Round bar, Flat bar, Bolts and Nuts X35Mn18 Ring forging, Heat treatment, 100% UT
MATERIAL DATASHEET - Grade X35Mn18
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS - DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.30 ~ 0.40
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 19.0 ~ 22.0
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 19.0 ~ 22.0
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): -
Nickle, Ni (％): ≤ 1.00
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.10
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.10
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150~950℃
Quenching or solution treatment temperature: 1000~1100℃
Tensle strength, σb≥ /MPa: 650900
Yield strength, σ0.2 ≥/MPa: 240
Reduction of area, δ≥(％): 22.0
Impact, Akv ≥/J: 55 (transversal value)
Yield strength, σ0.2 ≥/MPa: 240
Reduction of area, δ≥(％): 22.0
Impact, Akv ≥/J: 55 (transversal value)
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
PROFILE AND DIMENSIONS AVAILABLE
The alloy is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
PROFILE AND DIMENSIONS AVAILABLE
Round bar & Disc (diameter): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 620mm
Square bar / Flat bar: 10mm to 620mm
Length: Fixed length or random length or based on the customer's special requirements.
Heavy/middle plate via hot rolled: T60 - 350mm X W60 - 1100mm X Lmm
Forging piece: Different shapes based on OEM.
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：X35Mn18
Previous page：34CoCrMoV19-12
Last page：1.2890
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1