Austenitic Stainless Steel AMS 5507 Corrosion and Heat resistant, Sheet, Strip, and plate 17Cr - 13Ni - 2.5Mo (AISI 316L) Solution heat treated.
TECHNICAL DATA SHEET - AMS 5507
Stock available: Plate, Sheet, Strip
Material Category: Austenitic type 17Cr - 13Ni - 2.5Mo stainless
Stock available: Plate, Sheet, Strip
Material Category: Austenitic type 17Cr - 13Ni - 2.5Mo stainless
Material Specifications: AMS 5507G
H S Code For Customs: 7220 2030 / 7220 1200 / 7220.1100
AMS 5507 is usually produced by EAF + AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Material supply of condition: cold rolled, solution heat treated, and, unless solution heat treatment is performed in an atmosphere yielding a brightfinish, descaled having a surface appearance in accordance with ASTM A 480/A 480M.
H S Code For Customs: 7220 2030 / 7220 1200 / 7220.1100
AMS 5507 is usually produced by EAF + AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Material supply of condition: cold rolled, solution heat treated, and, unless solution heat treatment is performed in an atmosphere yielding a brightfinish, descaled having a surface appearance in accordance with ASTM A 480/A 480M.
TYPICAL CHEMICAL ELEMENTS (mass weight - %)
Carbon, C (％): ≤ 0.030
Manganese, Mn (％): ≤ 2.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 16.00 ~ 18.00
Nickel, Ni (%): 10.00 ~ 14.00
Molydenum, Mo (%): 2.00 ~ 3.00
Copper, Cu (%): ≤ 0.75
Ferrum, Fe (%): balance.
Carbon, C (％): ≤ 0.030
Manganese, Mn (％): ≤ 2.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 16.00 ~ 18.00
Nickel, Ni (%): 10.00 ~ 14.00
Molydenum, Mo (%): 2.00 ~ 3.00
Copper, Cu (%): ≤ 0.75
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Conditon: hot or cold rolled
Tensile strength, Rm ≥ MPa: 482 ~ 689
Yield strength, Ro0.2 / MPa: 172
Elongation, A5 ≥ (％): 40.0
Reduction of area, Z ≥ (％): -
Hardness via heat treatment / HRC: 39 ~ 46.
Reduction of area, Z ≥ (％): -
Hardness via heat treatment / HRC: 39 ~ 46.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：
Previous page：XT80W20Co12Cr4V2Mo1
Last page：最后一页