40X10C2M
2025-02-22 09:04:53 Origin： Remark：0 Click：
Material standard ГОСT 5632 -1972 Martensitic Stainless steel Wire rod, Round bar 40X10C2M Stock available, Application Diesel Engine Parts, Turbine engine development
MATERIAL DESIGNATION - 40X10C2M
Material Category - Stainless Steel & Heat resisting steel
Material technical standards: ГОСT 5632 -1972
Material Category - Stainless Steel & Heat resisting steel
Material technical standards: ГОСT 5632 -1972
Available in stock - Round bar diameter 6.0 ~ 60mm
Typical chemical compositions (mass weight - %)
Carbon, C (％): 0.35 ~ 0.45
Silicon, Si (％): 1.90 ~ 2.60
Manganese, Mn (％): ≤ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 9.00 ~ 10.50
Nickel, Ni (%): ≤ 0.60
Molybdenum, Mo (％): 0.70 ~ 0.90
Titanium, Ti (%): ≤ 0.20
Ferrum, Fe (%): remainder.
Carbon, C (％): 0.35 ~ 0.45
Silicon, Si (％): 1.90 ~ 2.60
Manganese, Mn (％): ≤ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 9.00 ~ 10.50
Nickel, Ni (%): ≤ 0.60
Molybdenum, Mo (％): 0.70 ~ 0.90
Titanium, Ti (%): ≤ 0.20
Ferrum, Fe (%): remainder.
TYPICAL MECHANICAL PROPERTIES UNDER ROOM TEMP.
1) Heat treatment condition: Quenching 1010 ~ 1050℃, oil cooling, Tempering 720 ~ 780 ℃, oil cooling
Tensile strength, Rm ≥ MPa: 930
Yield strength, Rp0.2 ≥ MPa: 735
Elongation, A5 ≥ (％): 10.0
Reduction of area, Z (%): 35.0
Impact, AK/J ≥: 20
Yield strength, Rp0.2 ≥ MPa: 735
Elongation, A5 ≥ (％): 10.0
Reduction of area, Z (%): 35.0
Impact, AK/J ≥: 20
Hardness / HBW: 340 ~ 385
2) Annealing 780 ~ 820 ℃, furnace cooling
2) Annealing 780 ~ 820 ℃, furnace cooling
Tensile strength, Rm ≥ MPa: -
Yield strength, Rp0.2 ≥ MPa: -
Elongation, A5 ≥ (％): -
Reduction of area, Z (%): -
Yield strength, Rp0.2 ≥ MPa: -
Elongation, A5 ≥ (％): -
Reduction of area, Z (%): -
Hardness, HB: -
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Raw Material Stock Available
Custom 450 / GD450 / XM-25 (S45000), 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151D, FV520B / S143 / 1.4594. X22CrMoV12-1, AISI 690 / Refractaloy 26
AISI 615 / S41800, PH13-8 /XM-13 / S13800, 15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, S132, S131, S111, S159, S154.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Raw Material Stock Available
Custom 450 / GD450 / XM-25 (S45000), 403 ESR, AISI 616 / 422 ESR, B50A365 / 403Cb+
17-4PH / 630, M-152 / 1.4938 / S151D, FV520B / S143 / 1.4594. X22CrMoV12-1, AISI 690 / Refractaloy 26
AISI 615 / S41800, PH13-8 /XM-13 / S13800, 15-5PH / XM-12 (S15500), A-286 AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, S132, S131, S111, S159, S154.
TECHNICAL SALES ASSISTANCE
If you are interested in our products or services, or would like to learn more about us, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Hot search：
Total list
Monthly rank
- 70Z15CN17-03
- 43ASTM A565 type 616HT
- 41P550
- 2810705MBU
- 27X2Cr11 / 1.4003
- 26Z10CNT18-11
- 24Magnadur 601
- 24ASTM A638 Gr.660
- 22FV535
- 22S42400