Martensite 12Cr-2Ni-2Mo-V Steel S64152 Round bars, Forgings, Flat bar M-152 ESR, hot forging, hot rolling, heat treatment, cold working & cold finishing.
TECHNICAL DATA SHEET - Grade UNS S64152
MATERIAL CATEGORY - Martensite type 12Cr-2Ni-2Mo-V-N
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - ASTM A565 (2004)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.08 ~ 0.15
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Niobium, Nb (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Vanadium, V (%): 0.25 ~ 0.40
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Niobium, Nb (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Vanadium, V (%): 0.25 ~ 0.40
Nitrogen, N (%): 0.01 ~ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: annealed
Tensile strength, σb/MPa: -
Yield strength, σ0.2/MPa: -
Yield strength, σ0.2/MPa: -
Elongation, δ(％): -
Reduction of area, ф(％): -
Hardness | HB: ≤ 311
Reduction of area, ф(％): -
Hardness | HB: ≤ 311
Condition of heat treatment:
Quenched 955℃~1022℃ air/oil cooling, >=565℃ X 2h tempered
Tensile strength, σb/MPa: 1000
Yield strength, σ0.2/MPa: 795
Yield strength, σ0.2/MPa: 795
Elongation, δ(％): 17.0
Reduction of area, ф(％): 35.0
Hardness | HB: 302 ~ 352
Reduction of area, ф(％): 35.0
Hardness | HB: 302 ~ 352
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
PROFILE & DIMENSIONS AVAILABLE
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to E-MAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to E-MAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：S64152
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1