Technical specifications of UNS S50300 Martensite steel S50300 Round bar, Flat bar, Plate Steelmaking, forging, rolling, heat treatment, cold working.
MATERIAL DATA SHEET - AISI 503 & UNS S50300
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.040
Chromium, Cr (%): 6.00 ~ 8.00
Nickel, Ni (%): -
Molybdenum, Mo (%): 0.45 ~ 0.65
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.040
Chromium, Cr (%): 6.00 ~ 8.00
Nickel, Ni (%): -
Molybdenum, Mo (%): 0.45 ~ 0.65
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: QT
Tensile strength, σb / MPa: 630
Yield strength, σ0.2 / MPa: 540
Elongation, δ (%): 14.0
ф (%): -
Hardness | HRB: ---
ф (%): -
Hardness | HRB: ---
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
TYPICAL APPLICATIONS
Chemical equipment and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 3000mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, and other different shapes based on OEM.
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, and other different shapes based on OEM.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1