S13800
2014-10-28 11:24:22 Origin： Remark：0 Click：
Description S13800 Plate, Forgings S13800 Flat bars, Stocklist S13800 Sheet Round bar Property Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade S13800
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS - ASTM A693 (2003)
MATERIAL SPECIFICATIONS - ASTM A693 (2003)
INVENTORY ON SALE - Flat bar 41/81 X 650 X Lmm, Round bar dia. 50mm, 60mm
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
Others (%): N ≤ 0.01
MECHANICAL PROPERTIES UNDER DIFFERENT AGEING TEMPERATURES
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1410
Yield strength, σ0.2≥/MPa: 1312
Elongation, δ≥(％): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
TS, σb≥/MPa: 1275
YS, σ0.2≥/MPa: 1200
EL, δ≥(％): 11.0
Hardness |HRC: 41
MECHANICAL PROPERTIES UNDER DIFFERENT AGEING TEMPERATURES
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1410
Yield strength, σ0.2≥/MPa: 1312
Elongation, δ≥(％): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
TS, σb≥/MPa: 1275
YS, σ0.2≥/MPa: 1200
EL, δ≥(％): 11.0
Hardness |HRC: 41
MATERIAL CATEGORY - Martensitic precipitation hardening stainless steel, 13-8 stainless alloy (S13800) is a martensitic precipitation-hardening stainless steel that has excellent strength, high hardness, superior toughness, and good corrosion resistance.
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in solution annealed condition.
Final heat treatment - solution + ageing treated
TYPICAL APPLICATIONS
A high level of useful mechanical properties under severe environmental conditions. Alloy 13-8 Stainless Steel is used in aerospace components, landing gear, nuclear reactor components, petrochemical industry, injection molding equipment etc. Alloy 13-8 Stainless Steel in the annealed condition can be strengthened further by relatively low temperature heat treatment.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 800mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 500mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in solution annealed condition.
Final heat treatment - solution + ageing treated
TYPICAL APPLICATIONS
A high level of useful mechanical properties under severe environmental conditions. Alloy 13-8 Stainless Steel is used in aerospace components, landing gear, nuclear reactor components, petrochemical industry, injection molding equipment etc. Alloy 13-8 Stainless Steel in the annealed condition can be strengthened further by relatively low temperature heat treatment.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 800mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 500mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Other different shapes based on OEM.
ADVANTAGE & SUPERIOR SERVICE
17+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com
17+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com
Hot search：S13800
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1