PH13-8Mo
2014-10-29 17:07:38 Origin： Remark：0 Click：
Description PH13-8Mo Plate, Inventory PH13-8Mo Flat bars, Shaft PH13-8Mo Round bars property from Steelmaking, ESR melting, Hot blooming, UT, Hot forging/rolling, Heat treated, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATA SHEET - Alloy PH13-8Mo & XM-13 & UNS S13800
MATERIAL CATEGORY - Precipitation hardening type 13Cr-8Ni-2Mo-Al
MATERIAL CATEGORY - Precipitation hardening type 13Cr-8Ni-2Mo-Al
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT / Ageing treated
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A693, A705
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT / Ageing treated
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A693, A705
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
N (%): ≤ 0.01
MECHANICAL PROPERTIES (Ageing treated)
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1410
Yield strength, σ0.2≥/MPa: 1312
Elongation, δ≥(％): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1275
Yield strength, σ0.2≥/MPa: 1200
Elongation, δ≥(％): 11.0
Hardness |HRC: 41
Ageing teated: H1050, 565℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1200
Yield strength, σ0.2≥/MPa: 1135
Elongation, δ≥(％): 12.0
Hardness |HRC: 40
Ageing teated: H1100, 595℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1030
Yield strength, σ0.2≥/MPa: 930
Elongation, δ≥(％): 14.0
Hardness |HRC: 34
Ageing teated: H1150, 620℃, 4h, air cooling
Tensile strength, σb≥/MPa: 930
Yield strength, σ0.2≥/MPa: 625
Elongation, δ≥(％): 14.0
Hardness |HRC: 30
MECHANICAL PROPERTIES (Ageing treated)
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1410
Yield strength, σ0.2≥/MPa: 1312
Elongation, δ≥(％): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1275
Yield strength, σ0.2≥/MPa: 1200
Elongation, δ≥(％): 11.0
Hardness |HRC: 41
Ageing teated: H1050, 565℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1200
Yield strength, σ0.2≥/MPa: 1135
Elongation, δ≥(％): 12.0
Hardness |HRC: 40
Ageing teated: H1100, 595℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1030
Yield strength, σ0.2≥/MPa: 930
Elongation, δ≥(％): 14.0
Hardness |HRC: 34
Ageing teated: H1150, 620℃, 4h, air cooling
Tensile strength, σb≥/MPa: 930
Yield strength, σ0.2≥/MPa: 625
Elongation, δ≥(％): 14.0
Hardness |HRC: 30
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Shaft, Valve.
Motocycle parts.
PRODUCT SHAPES AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 550mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Shaft, Valve.
Motocycle parts.
PRODUCT SHAPES AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 550mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com
Hot search：PH13-8Mo
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1