ALLOY MATERIAL DATA SHEET - UNS S15700
MATERIAL CATEGORY - Precipitation hardening type 15Cr-7Ni-2Mo-Al
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580, A564
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.09
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 14.0 ~ 16.0
Nickel, Ni (％): 6.50 ~ 7.75
Molybdenum, Mo (％): 2.00 ~ 3.00
Aluminum, Al (％): 0.75 ~ 1.50
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 14.0 ~ 16.0
Nickel, Ni (％): 6.50 ~ 7.75
Molybdenum, Mo (％): 2.00 ~ 3.00
Aluminum, Al (％): 0.75 ~ 1.50
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: bar, forge piece
Condition: RH950
Tensile strength, σb/MPa: 1380
Yield strength, σ0.2/MPa: 1210
Elongation, δ (％): 7.0
Reduction of area, ψ (％): 25.0
HRC: —
Tensile strength, σb/MPa: 1380
Yield strength, σ0.2/MPa: 1210
Elongation, δ (％): 7.0
Reduction of area, ψ (％): 25.0
HRC: —
Form: bar,forge piece
Condition: RH1050
σb/MPa: 1240
σ0.2/MPa: 1100
δ (％): 8.0
ψ (％): 25.0
σ0.2/MPa: 1100
δ (％): 8.0
ψ (％): 25.0
HRC: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TYPICAL APPLICATIONSRound bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Chemical equipment and parts.
Mechanical parts used in the condition of corrosion resistance,
Bolt and nuts and Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Hot search：S15700
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1