A564 Grade XM-13
2014-10-29 20:49:49 Origin： Remark：0 Click：
ASTMA564 Technical specifications Precipitation hardening steel XM-13 Round bar S13800 Plate stock. Flat bar XM-13 Hot forging / rolling, heat treatment, cold working.
MATERIAL DATA SHEET - PH13-8Mo / ASTM XM-13 / UNS S13800
MATERIAL CATEGORY: Precipitation hardening type 13Cr-8Ni-2Mo-Al
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
AVAILABILITY
Round bar / flat bar / steel strip / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (WEIGHT %)
Carbon, C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
Phosphorus, P (％)≤: 0.010
Sulfur, S (％)≤: 0.008
Chromium, Cr (％): 12.3 ~ 13.2
Nickel, Ni (％): 7.50 ~ 8.50
Molybdenum, Mo (％): 2.00 ~ 2.50
Aluminum, Al (％): 0.90 ~ 1.35, N ≤ 0.01
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Form: Bar, forge piece
Condition: H950
Tensile strength, σb/MPa: 1510
Yiled strength, σ0.2/MPa: 1420
Elongation, δ (％): 10
Reduction of erea, ψ (％): 45；35
Hardness, HRC: ≥45
Condition: H950
Tensile strength, σb/MPa: 1510
Yiled strength, σ0.2/MPa: 1420
Elongation, δ (％): 10
Reduction of erea, ψ (％): 45；35
Hardness, HRC: ≥45
Form: Bar, forge piece
Condition: H1000
σb/MPa: 1410
σ0.2/MPa: 1310
δ (％): 10
ψ (％): 50；40
HRC: ≥43
σ0.2/MPa: 1310
δ (％): 10
ψ (％): 50；40
HRC: ≥43
Form: Bar, forge piece
Condition: H1025
σb/MPa: 1275
σ0.2/MPa: 1210
δ (％): 11
σ0.2/MPa: 1210
δ (％): 11
ψ (％): 50；45
HRC: ≥41
HRC: ≥41
Form: Bar, forge piece
Condition: H1050
σb/MPa: 1210
σ0.2/MPa: 1140
δ (％): 12
ψ (％): 50；45
HRC: ≥40
σ0.2/MPa: 1140
δ (％): 12
ψ (％): 50；45
HRC: ≥40
Form: Bar, forge piece
Condition: H1100
σb/MPa: 1030
σ0.2/MPa: 930
δ (％): 14
ψ (％): 50
HRC: ≥34
σ0.2/MPa: 930
δ (％): 14
ψ (％): 50
HRC: ≥34
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5 to 500mm
Square bar / Flat bar: 10 to 650mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 10 to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts /other different shapes based on OEM.
Square bar / Flat bar: 10 to 650mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 10 to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1