S35500
2014-11-03 11:26:13 Origin： Remark：0 Click：
Precipitation hardening steel S35500 Round bar, Flat bar, Forgings S35500 Steelmelting (ESR refined), Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - S35500
MATERIAL CATEGORY - Precipitation hardening type 15Cr-4Ni-3Mo-N
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged.
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580, A564
CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.25
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 16.0
Nickel, Ni (％): 4.00 ~ 5.00
Molybdenum, Mo (％): 2.50 ~ 3.25
Nitrogen, N (％): 0.07 ~ 0.13
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.25
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 16.0
Nickel, Ni (％): 4.00 ~ 5.00
Molybdenum, Mo (％): 2.50 ~ 3.25
Nitrogen, N (％): 0.07 ~ 0.13
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: plate,sheet,strip
Condition: H850
Tensile strength, Rm / MPa: 1310
Yield strength, Rp0.2 / MPa: 1140
Elongation, A5 (％): 10.0
Reduction in area, Z, ф (％): -
Elongation, A5 (％): 10.0
Reduction in area, Z, ф (％): -
Hardness | HRB: -
Form: plate, sheet, strip
Condition: H1000
σb / MPa: 1170
σ0.2 / MPa: 1030
δ (％): 12
ф (％): -
δ (％): 12
ф (％): -
Hardness | HRB: ≥37
Form: forge piece
Condition: H1000
σb / MPa: 1170
σ0.2 / MPa: 1070
σ0.2 / MPa: 1070
δ (％): 12
ф (％): 25
Hardness | HRB: ≥37
PROFILE & DIMENSIONS
ф (％): 25
Hardness | HRB: ≥37
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：S35500
Previous page：AISI 634
Last page：17-7PH / AISI 631
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1