2024-12-03 10:50:00 Origin: Remark:0 Click:
XM-25 / S45000 is A Martensitic Precipitation hardening 15Cr-6Ni-Mo-1Cu Stainless steel, S45000 offers good properties available Round bar, flat bar, and forgings.
TECHNICAL DATA SHEET - XM-25 & S45000
MATERIAL CATEGORY - Precipitation hardening type 15Cr-6Ni-Mo-1Cu
INVENTORY AVAILABLE - Round bar, diameter 20 ~ 200mm, ESR ingot
MELTING PRACTICE - EAF + LF + VD / + EF + ESR / VAR
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A564
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (%): ≤ 0.05
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 14.0 ~ 16.0
Nickel, Ni (%): 5.00 ~ 7.00
Molybdenum, Mo (%): 0.50 ~ 1.00
Copper, Cu (%): 1.25 ~ 1.75
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 14.0 ~ 16.0
Nickel, Ni (%): 5.00 ~ 7.00
Molybdenum, Mo (%): 0.50 ~ 1.00
Copper, Cu (%): 1.25 ~ 1.75
Niobium, Nb (%): ≥ 8 × C
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: round bar, flat bar, forgings
Condition: annealed
Tensile strength, Rm / MPa: 895
Yield strnegth, Rp0.2 / MPa: 655
Elongation, A5 (%): 10.0
Reduction of area, Z (%): 40
Elongation, A5 (%): 10.0
Reduction of area, Z (%): 40
Hardness | HRC: 32min.
Form: forge piece
Condition: annealed
Tensile strength, Rm / MPa: 860
Yield strength, Rp0.2 / MPa: 655
Elongation, A5 (%): 10.0
Reduction of area, Z (%): 40.0
Elongation, A5 (%): 10.0
Reduction of area, Z (%): 40.0
Hardness | HRC: 33min
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - 1040℃ solution treated + 480 ~ 620 ℃ aged.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance
Bolt and nut, Pressure vessel.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - 1040℃ solution treated + 480 ~ 620 ℃ aged.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance
Bolt and nut, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / rod / disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 8mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped, other different shapes based on OEM.
Round bar / rod / disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 8mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search: XM-25
Previous page:Custom 450
Last page:S45000
Total list
Monthly rank
- 48ASTM A565 Gr.616HT
- 20Z50NMC12
- 20EN 58B
- 19S42400
- 18ASTM A890 Grade 1B
- 18Z10CNW17
- 16SAE 51416
- 16SAE J405
- 15St T17/13W
- 151.4300 / X12CrNi18-8