Martensitic Precipitation hardening Steel S45000 & XM-25 Round bar, flat bar, S45000 ESR ingot, Steelmaking, Hot forging / rolling, Heat treatment
MATERIAL DATA SHEET - UNS S45000
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
INVENTORY STOCK - Round bar diameter 20 ~ 200mm
MELTING PRACTICE - EAF + AOD + ESR / VAR
MATERIAL CATEGORY - 15Cr - 6Ni - 2Cu Martensitic stainless
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 14.0 ~ 16.0
Nickel, Ni (％): 5.00 ~ 7.00
Molybdenum, Mo (％): 0.50 ~ 1.00
Copper, Cu (％): 1.25～1.75
Others (%): Nb ≥ 8 × C
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 895
Yield strength, σ0.2 / MPa: 655
Elongation, δ5 ≥ (％): 10.0
Reduction of area, ф ≥ (％): 40.0
Hardness via heat treatment /HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment + Aged.
TYPICAL APPLICATIONS
Chemical equipment & Parts.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
AVAILABLE FORMS AND DIMENSIONS
Round bar / rod / disc (diameter): 5.5 ~ 550mm
Square bar / Flat bar: 10 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
MATERIAL CATEGORY - 15Cr - 6Ni - 2Cu Martensitic stainless
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 14.0 ~ 16.0
Nickel, Ni (％): 5.00 ~ 7.00
Molybdenum, Mo (％): 0.50 ~ 1.00
Copper, Cu (％): 1.25～1.75
Others (%): Nb ≥ 8 × C
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 895
Yield strength, σ0.2 / MPa: 655
Elongation, δ5 ≥ (％): 10.0
Reduction of area, ф ≥ (％): 40.0
Hardness via heat treatment /HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment + Aged.
TYPICAL APPLICATIONS
Chemical equipment & Parts.
Mechanical parts used in the condition of corrosion resistance.
Bolts and nuts, Pressure vessel.
AVAILABLE FORMS AND DIMENSIONS
Round bar / rod / disc (diameter): 5.5 ~ 550mm
Square bar / Flat bar: 10 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：S45000
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1