Precipitation hardened stainless steel AISI 665 Round bar, flat bar, and S66545 Forgings ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test .
TECHNICAL DATA SHEET - Grade AISI 665 & S66545
TECHNICAL SPECIFICATIONS - ASTM A240 (2004), A276, A580
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Precipitation hardened stainless steel
CHEMICAL COMPOSITION (mass weight %)
TECHNICAL SPECIFICATIONS - ASTM A240 (2004), A276, A580
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Precipitation hardened stainless steel
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): 0.10 ~ 0.80
Manganese, Mn (％): 1.25 ~ 2.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 15.0
Nickel, Ni (％): 24.0 ~ 28.0
Molybdenum, Mo (％): 1.25 ~ 2.25
Nitroge, N (&): -
Silicon, Si (％): 0.10 ~ 0.80
Manganese, Mn (％): 1.25 ~ 2.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 15.0
Nickel, Ni (％): 24.0 ~ 28.0
Molybdenum, Mo (％): 1.25 ~ 2.25
Nitroge, N (&): -
Titanium, Ti (%): 2.70 ~ 3.30
Boron, B (%): 0.01 ~ 0.07
Others (％): Cu ≤0.25, Al ≤0.25
Others (％): Cu ≤0.25, Al ≤0.25
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, plate, and forgings
Tensile strength, σb/MPa: 750
Yield strength, σ0.2/MPa: 350
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness (HBW): -
METHOD OF MELTING
The alloy is usually produced by BEF - AOD / EAF + VD = LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 450mm
Flat bar / plate (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email sales@ccsteels.com.
Form: Bar, plate, and forgings
Tensile strength, σb/MPa: 750
Yield strength, σ0.2/MPa: 350
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness (HBW): -
METHOD OF MELTING
The alloy is usually produced by BEF - AOD / EAF + VD = LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 450mm
Flat bar / plate (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email sales@ccsteels.com.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1