316LVM
2014-11-05 09:41:38 Origin： Remark：0 Click：
Austenitic Stainless steel 316LVM, has been used for permanent implants. Round bar, flat bar, S31673 VAR Melted, hot forging, hot rolling, heat treatment, cold working.
MATERIAL DATA SHEET - ASTM 316LVM & UNS S31673
MATERIAL CATEGORY - Austenitic stainless steel - 18Cr-15Ni-3Mo
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment.
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580, A564
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.025
S (％)≤: 0.010
Cr (％): 17.0 ~ 19.0
Ni (％): 13.0 ~ 15.5
Mo (％): 2.50 ~ 3.20
Others (％): N ≤ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.025
S (％)≤: 0.010
Cr (％): 17.0 ~ 19.0
Ni (％): 13.0 ~ 15.5
Mo (％): 2.50 ~ 3.20
Others (％): N ≤ 0.10
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: Plate,sheet, strip
Tensile strength, σb/MPa: 1400~1800
Yield strength, σ0.2/MPa: -
Elongation, δ(％): 50.0
Reduction of area, ф(％): -
Elongation, δ(％): 50.0
Reduction of area, ф(％): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: N
Stainless Steel Rod, Bar, Wire, Cold drawn, ground and polished
Standard length of bars: 2 - 3 meter.
Austenitic Stainless Steel for implants, with high corrosion resistance.
According to ISO 5832/1, F-138 Vacuum melt grade (VAR)
For surgical instruments, fracture fixation devices, screws for implants and many more similar applications.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Hot search：316LVM
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1