Technical specifications of DIN X7Cr14 Stainless steel 1.4001 Round bar, Flat bar, Plate, Stock Available steelmaking, Hot forging, rolling, Heat treatment
MATERIAL DATA SHEET - DIN X7Cr14 & W-Nr 1.4001
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Ferrum, Fe (％): balance
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Ferrum, Fe (％): balance
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealing
Tensile strength, Rm / MPa: -
Yield strength, Rp σ0.2 ≥ / MPa: 245
Elongation, A5 ≥ (％): 20
Yield strength, Rp σ0.2 ≥ / MPa: 245
Elongation, A5 ≥ (％): 20
Reduction of area, Z ≥ (％): 60
Impact strength, Akv ≥/J: -
Hardness HBS30: 130 ~ 180
Impact strength, Akv ≥/J: -
Hardness HBS30: 130 ~ 180
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1150 ~ 750
Heat treatment temperature and cooling methods|annealing: 750 ~ 800 furnace cooling
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 235
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 226
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 226
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 221
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 198
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 198
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment and parts.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Disc (Diameter): 5.50mm to 800mm
Square bar / Flat bar: 6mm to 600mm
Round bar / Disc (Diameter): 5.50mm to 800mm
Square bar / Flat bar: 6mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate: T3 - 200mm X W60 - 1500mm X L1000-12000mm
Sheet steel: T0.5 - 3mm X W20 - 1000mm X L1000 - 2000mm
Steel strip: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Hot search：
Previous page：1.4000
Last page：X6CrAl13 / 1.4002
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1