2014-11-11 14:37:37 Origin： Remark：0 Click：
Technical specifications of DIN X6CrAl13 Ferritic steel, 1.4002 Round bar, plate, flat bar, hot forging, rolling, heat treatment, cold working.
MATERIAL DATA SHEET - DIN X6CrAl13 & W-Nr 1.4002
MATERIAL CATEGORY: Ferritic stainless steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％)≤: 1.00
Manganese, Mn (％)≤: 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Aluminum, Al (％): 0.10 ~ 0.30
Silicon, Si (％)≤: 1.00
Manganese, Mn (％)≤: 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Aluminum, Al (％): 0.10 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealing
Thickness/mm: -
Thickness/mm: -
Tensile strength, σb/MPa: 400 ~ 600
Yield strength, σ0.2≥/MPa: 250
Elongation, δ5≥(％): 20
Yield strength, σ0.2≥/MPa: 250
Elongation, δ5≥(％): 20
Reduction of area, ψ≥(％): 60
Impact strength, Akv≥/J: -
Hardness HBS30: ≤185
Impact strength, Akv≥/J: -
Hardness HBS30: ≤185
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 750 ~ 800 water cooling
Heat treatment temperature and cooling methods|quenching: 950 ~ 1000 air / oi cooling
Heat treatment temperature and cooling methods|tempering: 650 ~ 750
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 235
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 225
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 225
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 220
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 195
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 195
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments and parts.
Chemical equipments, Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 400mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate: T3 - 200mm X W600- 2500mm X L1000-12000mm
Sheet steel: T0.5 - 3mm X W200- 1000mm X L1000 - 2000mm
Steel strip: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：X7Cr14 / 1.4001
Last page：DIN X2CrNi12
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1