X2Cr11 / 1.4003
2014-11-11 14:49:32 Origin： Remark：0 Click：
Specifications Martensitic Steel X2Cr11 Round bar, Inventory 1.4003 Flat bar, Stocklist 1.4003 Plate steelmaking, heat treatment, cold worked
TECHNICAL DATA SHEET - DIN X2Cr11 & W-Nr 1.4003
MATERIAL CATEGORY - Martensitic Stainless steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Q + T
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Q + T
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％) ≤: 1.00
Manganese, Mn (％) ≤: 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 10.5 ~ 12.5
Nickel, Ni (％): 0.30 ~ 1.00
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.030
Silicon, Si (％) ≤: 1.00
Manganese, Mn (％) ≤: 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 10.5 ~ 12.5
Nickel, Ni (％): 0.30 ~ 1.00
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.030
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: 100
Thickness/mm: 100
Tensile strength, Rm / MPa: 450 ~ 600
Yield strength, Rp0.2 ≥ MPa: 260
Elongation, δ5 ≥ (％): 20.0
Yield strength, Rp0.2 ≥ MPa: 260
Elongation, δ5 ≥ (％): 20.0
Reduction of area, Z ≥ (％): -
Impact strength, Akv ≥ J: -
Hardness HBS30: 200 max.
Impact strength, Akv ≥ J: -
Hardness HBS30: 200 max.
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 680 ~ 740 water cooling
Heat treatment temperature and cooling methods|quenching: 950~ 1000 air / oi cooling
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 240
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 220
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 220
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 210
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE & DIMENSIONS
Round bar / rod / disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 8mm to 600mm
Square bar / Flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate: T3 - 200mm X W60 - 1500mm X L1000-12000mm
Sheet steel: T0.5 - 3mm X W20 - 1000mm X L1000 - 2000mm
Steel strip: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TYPICAL APPLICATIONS
Medical equipments and parts.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Previous page：DIN X2CrNi12
Last page：DIN X12CrS13
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1