1.4005 / X12CrS13
2014-11-11 16:17:11 Origin： Remark：0 Click：
Technical specifications of DIN 1.4005 / X12CrS13 Stainless steel, Round bar, Flat bar, Plate 1.4005 / X12CrS13 Steelmaking, Hot forging,rolling, Heat treatment
TECHNICAL DATA SHEET - DIN X12CrS13 & W-Nr 1.4005
MATERIAL CATEGORY: Martensitic Steel Series.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass fraction - %)
Carbon, C (％): 0.08 ~ 0.15
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.15 ~ 0.25
Chromium, Cr (％): 12.0 ~ 13.0
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.15 ~ 0.25
Chromium, Cr (％): 12.0 ~ 13.0
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: HT
Thickness/mm: 160
Thickness/mm: 160
Tensile strength, Rm / MPa: 650～850
Yeild strength, Rpσ0.2 ≥ MPa: 450
Yeild strength, Rpσ0.2 ≥ MPa: 450
Elongation, A5 ≥ (％): 12
Reduction of area, ψ ≥ (％): 45
Impact strength, Akv ≥ J: -
Hardness HBS30: -
Impact strength, Akv ≥ J: -
Hardness HBS30: -
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 745 ~ 825 air cooling
Heat treatment temperature and cooling methods|quenching: 950~ 1000 oil cooling
Heat treatment temperature and cooling methods|tempering: 680~780
Condition: HT
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (diameter): 0.50mm to 500mm
Square bar / Flat bar: 8mm to 400mm
Round bar / Wire rod (diameter): 0.50mm to 500mm
Square bar / Flat bar: 8mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate: T3 - 200mm X W60 - 1500mm X L1000-12000mm
Sheet steel: T0.5 - 3mm X W20 - 1000mm X L1000 - 2000mm
Steel strip: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：
Previous page：DIN X12CrS13
Last page：1.4006
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1