X6Cr17 / 1.4016
2025-02-18 17:02:00 Origin： Remark：0 Click：
Technical specifications of DIN X6Cr17 / 1.4016 Stainless steel, Round bar, Plate, Flat bar 1.4016 from steelmaking,hot forging, rolling, heat treatment, cold working
TECHNICAL DATA SHEET - X6Cr17 & 1.4016
MATERIAL CATEGORY: ferritic stainless steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - QT.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - QT.
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
TYPICAL CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0～18.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Ferrum, Fe (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0～18.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Ferrum, Fe (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness / mm: 100
Thickness / mm: 100
Tensile strength, σb / MPa: 400 ~ 630
Yield strength, σ0.2 ≥ MPa: 240
Elongation, δ5 ≥ (％): 20
Yield strength, σ0.2 ≥ MPa: 240
Elongation, δ5 ≥ (％): 20
Reduction of area, ψ ≥ (％): 60
Impact strength, Akv ≥ J: -
Hardness HBS30: 200max
Impact strength, Akv ≥ J: -
Hardness HBS30: 200max
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 750 ~ 800 air cooling
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 220
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 210
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 210
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 200
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：X6Cr17/DIN 1.4016
Total list
Monthly rank
- 52Z15CN17-03
- 36P550
- 33ASTM A565 type 616HT
- 22X2Cr11 / 1.4003
- 2110705MBU
- 20ASTM A638 Gr.660
- 19S42400
- 17Z8CND17-04
- 16Magnadur 601
- 16SAE 51420