X30Cr13
2014-11-13 13:26:50 Origin： Remark：0 Click：
Specifications of DIN X30Cr13 Martensitic Stainless steel, 1.4028 Round bar, flat bar, Forging, rolling, heat treatment, cold working.
TECHNICAL DATA SHEET - DIN X30Cr13 / DIN 1.4028
MATERIAL CATEGORY - Martensitic type
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT.
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.26 ~ 0.35
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Other (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Other (％): -
MECHANICAL PROPERTIES AT ROOM TEMPERATURE
Condition: annealed
Thickness/mm: -
Thickness/mm: -
Tensile strength, σb/MPa: 800 max.
Yield strength, σ0.2≥/MPa: -
Elongation, δ5 ≥(％): -
Yield strength, σ0.2≥/MPa: -
Elongation, δ5 ≥(％): -
Reduction of area, ψ≥ (％): -
Impact strength, Akv≥/J: -
Hardness HBS30: -
Impact strength, Akv≥/J: -
Hardness HBS30: -
Condition: HT
Thickness/mm: 160
Thickness/mm: 160
σb/MPa: 850 ~1000
σ0.2≥/MPa: 650
δ5≥(％): 10
σ0.2≥/MPa: 650
δ5≥(％): 10
ψ≥(％): -
Akv≥/J: -
Hardness HBS30: -
Akv≥/J: -
Hardness HBS30: -
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 745 ~ 825 air cooling
Heat treatment temperature and cooling methods|quenching: 850~1050 air or oil cooking
Heat treatment temperature and cooling methods|tempering: 625~675
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipments and parts.
Chemical equipments.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel.
INVENTORY - rolled / Disc
Bar -dia.: 10 - 850mm
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：X30Cr13
Previous page：K93120
Last page：X30Cr13 / 1.4028
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1