X39Cr13 Stainless, Chemical X39Cr13, Properties X39Cr13 steelmaking, hot forging, hot rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing.
MATERIAL DATA SHEET - DIN X39Cr13
MATERIAL CATEGORY: Common alloy steel - Martensitic type
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.36 ~ 0.42
Si (%): ≤ 1.00
Mn (%): ≤ 1.00
P (%)≤: 0.040
S (%)≤: 0.030
Cr (%): 12.5 ~ 14.5
Ni (%): -
Mo (%): -
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm: -
Tensile strength, σb/MPa: 800 max.
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(%): -
Reduction of area, ψ≥(%): -
Impact strength, Akv≥/J: -
Hardness HBS30: -
Si (%): ≤ 1.00
Mn (%): ≤ 1.00
P (%)≤: 0.040
S (%)≤: 0.030
Cr (%): 12.5 ~ 14.5
Ni (%): -
Mo (%): -
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm: -
Tensile strength, σb/MPa: 800 max.
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(%): -
Reduction of area, ψ≥(%): -
Impact strength, Akv≥/J: -
Hardness HBS30: -
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 750 ~ 850 air/furnace cooling
Heat treatment temperature and cooling methods|quenching: 850~1050 air or oil cooking
Heat treatment temperature and cooling methods|tempering: 100~200
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT AVAILABLE PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search:X39Cr13
Previous page:X30Cr13 / 1.4028
Last page:1.4031
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1