DIN EN 10088-1 Specifications X17CrNi16-2 Round bar, Flat bar, Forgings W-Nr. 1.4057 Hot forging, Hot rolling, Heat treatment, 100% Ultrasonic flaw detection test, Cold machined.
TECHNICAL DATA SHEET - Grade X17CrNi16-2
MATERIAL CATEGORY - Martensitic type
MATERIAL SPECIFICATIONS - DIN EN 10088-1, 10297, 10272, 10312
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.12 ~ 0.22
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%)≤: 0.040
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 15.0 ~ 17.0
Nickel, Ni (%): 1.50 ~ 2.50
Molybdenum, Mo (%): -
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%)≤: 0.040
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 15.0 ~ 17.0
Nickel, Ni (%): 1.50 ~ 2.50
Molybdenum, Mo (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: -
Thickness/mm: -
Tensile strength, σb/MPa: 950 max.
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(%): -
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(%): -
Reduction of area, ψ≥(%): -
Impact strength, Akv≥/J: -
Hardness HBS30: 295
Impact strength, Akv≥/J: -
Hardness HBS30: 295
Condition: HT
Thickness/mm: 60/160
Thickness/mm: 60/160
TS, σb/MPa: 800 ~ 950
YS, σ0.2≥/MPa: 600
EL, δ5≥(%): 14/12
EL, δ5≥(%): 14/12
RA, ψ≥(%): 45
Akv≥/J: 25/20
Hardness HBW30: -
Akv≥/J: 25/20
Hardness HBW30: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose.Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose.Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
TYPICAL APPLICATIONS
Medical equipments and parts, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Bolt and nuts, Pressure vessel.
FORMS & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Disc (diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 500mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Hot search:X17CrNi16-2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1