Martensitic Steel 1.4057 Round bar, flat bar, forgings X17CrNi16-2 ESR Hot forging, Hot rolling, Heat treatment, Cold working or machined.
MATERIAL TECHNICAL DATA SHEET - Grade W-Nr 1.4057
MATERIAL CATEGORY - Martensitic type
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by AOD / VOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN EN 10088-1, 10297,10272,10312
MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.12 ~ 0.22
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%)≤: 0.040
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 15.0 ~ 17.0
Nickel, Ni (%): 1.50 ~ 2.50
Molybdenum, Mo (%): —
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%)≤: 0.040
Sulfur, S (%)≤: 0.015
Chromium, Cr (%): 15.0 ~ 17.0
Nickel, Ni (%): 1.50 ~ 2.50
Molybdenum, Mo (%): —
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: -
Thickness/mm: -
Temsile strength, Rm MPa: 950 max.
Yield strength, Rp0.2 ≥ MPa: -
Elongation, A5 ≥(%): -
Yield strength, Rp0.2 ≥ MPa: -
Elongation, A5 ≥(%): -
Reduction of area, Z ≥ (%): -
Impact strength, Akv ≥ /J: -
Hardness HBS30: 295
Impact strength, Akv ≥ /J: -
Hardness HBS30: 295
Condition: HT
Thickness/mm: 60/160
Thickness/mm: 60/160
TS, σb/MPa: 800 ~ 950
YS, σ0.2≥/MPa: 600
EL, δ5≥(%): 14/12
EL, δ5≥(%): 14/12
RA, ψ≥(%): 45
Akv≥/J: 25/20
Hardness HBW30: -
Akv≥/J: 25/20
Hardness HBW30: -
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 730 ~ 800 air/furnace cooling
Heat treatment temperature and cooling methods|quenching: 980~1030 air or oil cooking
Heat treatment temperature and cooling methods|tempering: 100~300
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: -
TYPICAL APPLICATIONS
Medical equipments and parts.
Chemical equipments, Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Mechanical parts used in the condition of corrosion resistance.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 500mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Hot search:1.4057
Previous page:X17CrNi16-2
Last page:X14CrMoS17
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1