Specifications 1.4104 Stainless steel Round bar, Flat bar, Stock Available X14CrMoS17 properties from steelmaking, hot forging, hot rolling, heat treatment
MATERIAL DATA SHEET - W-Nr 1.4104
MATERIAL CATEGORY - Ferritic Type Staineless Steel
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / EAF Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.10 ~ 0.17
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.15 ~ 0.35
Chromium, Cr (%): 15.5 ~ 17.5
Nickel, Ni (%): -
Molybdenum, Mo (%): 0.20 ~ 0.60
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.50
Phosphorus, P (%) ≤: 0.040
Sulfur, S (%) ≤: 0.15 ~ 0.35
Chromium, Cr (%): 15.5 ~ 17.5
Nickel, Ni (%): -
Molybdenum, Mo (%): 0.20 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: -
Thickness/mm: -
Tensile strength, Rm / MPa: 730 max.
Yield strength, Rp0.2 ≥ MPa: 300
Elongation, A5 ≥ (%): 16
Yield strength, Rp0.2 ≥ MPa: 300
Elongation, A5 ≥ (%): 16
Reduction of area, Z ≥ (%): -
Impact strength, Akv ≥ J: -
Hardness HBS30: 220
Impact strength, Akv ≥ J: -
Hardness HBS30: 220
Condition: HT
Thickness/mm: 60/160
Thickness/mm: 60/160
Rm / MPa: 650 ~ 850
Rp0.2 ≥ MPa: 500
A5 ≥ (%): 12/10
A5 ≥ (%): 12/10
Z ≥ (%): 50
Akv ≥ /J: -
Hardness HBW30: -
Akv ≥ /J: -
Hardness HBW30: -
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: 750 ~ 850 air/furnace cooling
Heat treatment temperature and cooling methods|quenching: 990~1070 air or oil cooking
Heat treatment temperature and cooling methods|tempering: 550~650
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: -
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 400mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search:1.4104
Previous page:X14CrMoS17
Last page:X6CrMoS17
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1