Specifications X90CrMoV18 datasheet, X90CrMoV18 Chemical, X90CrMoV18 Property Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATA SHEET - DIN X90CrMoV18
MATERIAL CATEGORY - Martensitic and precipitation hardening corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.85 ~ 0.95
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): -
Mo (％): 0.90 ~ 1.30
V (％): 0.07 ~ 0.12
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): -
Mo (％): 0.90 ~ 1.30
V (％): 0.07 ~ 0.12
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: 100
Thickness/mm: 100
Tensile strength, σb/MPa: 830 max.
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: -
Hardness HBS30: 266
Impact strength, Akv≥/J: -
Hardness HBS30: 266
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: 780 ~ 840 furnace cooling
Heat treatment temperature and cooling methods|quenching: 1000~1050 oil cooling
Heat treatment temperature and cooling methods|tempering: 100~300
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / AVAILABILITY
Round bar / flat bar / steel strip / square bar / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / AVAILABILITY
Round bar / flat bar / steel strip / square bar / plate
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：X90CrMoV18
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1