1.4117 / X38CrMoV15
2014-11-16 09:36:38 Origin： Remark：0 Click：
Technical specifications of 1.4117 / 38CrMoV15 corrosion resisting steel stainless steel - Round bar, Flat bar, steelmaking, Hot forging / rolling, Heat treatment
TECHNICAL DATA SHEET - DIN X38CrMoV15 & W-Nr 1.4117
MATERIAL CATEGORY: Martensitic and precipitation hardening corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (％): 0.35 ~ 0.40
Silicon, Si (％) ≤: 1.00
Manganese, Mn (％) ≤: 1.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 14.0～15.0
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.40～0.60
Vanadium, V (％): 0.10～0.15
Silicon, Si (％) ≤: 1.00
Manganese, Mn (％) ≤: 1.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 14.0～15.0
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.40～0.60
Vanadium, V (％): 0.10～0.15
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: hardened
Thickness/mm:-
Thickness/mm:-
Tensile strength, Rm / MPa: -
Yield strength, Rp0.2 ≥ MPa:-
Elongation, A5 ≥ (％): -
Yield strength, Rp0.2 ≥ MPa:-
Elongation, A5 ≥ (％): -
Reduction of area, ψ ≥ (％): -
Impact strength, Akv ≥ J: -
Hardness HBS30: HRC 54 - 56
Impact strength, Akv ≥ J: -
Hardness HBS30: HRC 54 - 56
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 750 ~ 850 furnace cooled
Heat treatment temperature and cooling methods|quenching: 1000~1050 oil cooled
Heat treatment temperature and cooling methods|tempering: 100~200
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel.
Bolt and nut, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
PRODUCT PROFILE & DIMENSION
Round bar / Rod / Disc (diameter): 5.50mm to 800mm
Square bar / Flat bar: 8mm to 800mm
Round bar / Rod / Disc (diameter): 5.50mm to 800mm
Square bar / Flat bar: 8mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W100 - 1500mm X L1000-12000mm
Heavy/middle plate via hot rolled: T6 - 200mm X W100 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Hot search：
Previous page：X38CrMoV15
Last page：X20CrMo13
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1